T20, T25, T32, T40, T46, T60
T20 | T25 | T32 | T40 | T46 | T60 | ||
Apperance | 空白粉末 | ||||||
Ture密度 | 0.20g /cm3 | 0.25g /cm3 | 0.32g /cm3 | 0.40g /cm3 | 0.46g /cm3 | 0.60g /cm3 | |
FRA | 10th% | 32 | 30 | 30 | 20 | 22 | 18 |
50th% | 68 | 65 | 56 | 45 | 45 | 40 | |
90th% | 106 | 100 | 74 | 70 | 65 | 60 | |
易碎力量psi或Mpa | 550/4 | 750/5 | 2000/14 | 4000/28 | 6000/41 | 10000/69 | |
熔点 | 625℃ | 625℃ | 625℃ | 625℃ | 625℃ | 625℃ | |
浮动的比例 | 96% | 95% | 95% | 95% | 95% | 94% | |
酸碱度 | 8-9.5 | 8-9.5 | 8-9.5 | 8-9.5 | 8-9.5 | 8-9.5 |
索引 | ELT-2000 | ELT-4000 | ELT-6000 | ELT-8000 | ELT-12000 | |
Apperance | 空白粉末 | |||||
Ture密度 | 0.30-0.35 | 0.39-0.43 | 0.45-0.49 | 0.58-0.64 | 0.58-0.64 | |
FRA | 10th% | 25 | 25 | 25 | 22 | 22 |
50th% | 55 | 50 | 50 | 48 | 48 | |
90th% | 110 | 95 | 90 | 90 | 90 | |
易碎力量 psi或Mpa | 2000年 | 4000 | 6000 | 8000 | 12000 |
T20 | T25 | T32 | T40 | T46 | T60 | ||
Apperance | 空白粉末 | ||||||
Ture密度 | 0.20g /cm3 | 0.25g /cm3 | 0.32g /cm3 | 0.40g /cm3 | 0.46g /cm3 | 0.60g /cm3 | |
FRA | 10th% | 32 | 30 | 30 | 20 | 22 | 18 |
50th% | 68 | 65 | 56 | 45 | 45 | 40 | |
90th% | 106 | 100 | 74 | 70 | 65 | 60 | |
易碎力量psi或Mpa | 550/4 | 750/5 | 2000/14 | 4000/28 | 6000/41 | 10000/69 | |
熔点 | 625℃ | 625℃ | 625℃ | 625℃ | 625℃ | 625℃ | |
浮动的比例 | 96% | 95% | 95% | 95% | 95% | 94% | |
酸碱度 | 8-9.5 | 8-9.5 | 8-9.5 | 8-9.5 | 8-9.5 | 8-9.5 |
索引 | ELT-2000 | ELT-4000 | ELT-6000 | ELT-8000 | ELT-12000 | |
Apperance | 空白粉末 | |||||
Ture密度 | 0.30-0.35 | 0.39-0.43 | 0.45-0.49 | 0.58-0.64 | 0.58-0.64 | |
FRA | 10th% | 25 | 25 | 25 | 22 | 22 |
50th% | 55 | 50 | 50 | 48 | 48 | |
90th% | 110 | 95 | 90 | 90 | 90 | |
易碎力量 psi或Mpa | 2000年 | 4000 | 6000 | 8000 | 12000 |